      Al-Ti-C对Mg2Si/Al基复合材料组织及性能的影响

      Effect of Al-Ti-C on microstructure and mechanical properties of Mg2Si/Al alloy composites

      摘要:
      针对熔体反应法制备的原位自生Mg2Si/Al基复合材料组织粗大而导致合金性能降低现象,研究了添加不同质量的Al-Ti-C晶粒细化剂 (0, 0.1,0.3, 0.5, 1.0, 3.0, 5.0,10.0 wt%)对Mg2Si/Al基复合材料组织和性能的影响.结果表明,Al-Ti-C可使Mg2Si/Al基复合材料中的Mg2Si颗粒细化.当添加量为0.5 wt%时, Mg2Si颗粒由粗大菱角状变为细小圆滑状;但继续添加时会出现细化效果衰退现象.当Mg2Si晶粒细小、分布均匀时,Mg2Si/Al基复合材料的硬度高,摩擦性能更好.
      Abstract:
      For the coarse phase in in-situ Mg2Si/Al composites degraded the mechanical properties, the effect of Al-Ti-C grain refiner additions (0, 0.1,0.3, 0.5, 1.0, 3.0, 5.0 and 10.0 wt%) on the microstructure and mechanical properties of Mg2Si/Al composites were investigated.The results indicate the Mg2Si particles in Al matrix was refined by adding the Al-Ti-C master alloy.When the addition of Al-Ti-C was 0.5 wt%, the coarse and sharp Mg2Si particles were refined and smoothed.When the addition of Al-Ti-C was higher than 0.5 wt%, the refini effect was degraded.The Mg2Si/Al composites with finer and uniformly distributed reinforcement possess higher hardness and wear resistance.
      作者: 唐鹏 [1] 赵艳君 [1] 李睿 [2] 何建鑫 [2] 詹峰 [2]
      Author: TANG Peng [1] ZHAO Yan-jun [1] LI Rui [2] HE Jian-xin [2] ZHAN Feng [2]
      作者单位: 广西大学材料科学与工程学院, 广西南宁530004;广西生态型铝产业协同创新中心, 广西南宁530007 广西大学材料科学与工程学院,广西南宁,530004
      年,卷(期): 2017, 42(2)
      分类号: TG174.442
      在线出版日期: 2017年5月16日
      基金项目: 国家自然科学基金资助项目,广西自然科学基金资助项目,广西科学研究与技术开发重大专项计划,广西大学有色金属及材料加工新技术教育部重点实验室开放基金,"大学生创新创业训练计划"自治区级创新训练立项资助,广西生态型铝产业协同创新中心资助项目