      三缺位硅钨酸盐柱撑水滑石复合材料的制备及电化学行为

      Synthesis,Characterization and Electrochemical Performance of Polyoxometalates(β-SiW9)-Pillared Layered Double Hydroxide

      摘要:
      文章选用镁铝硝酸根型水滑石(LDH)和β-Na9H[SiW9O34]?21H2O (β-SiW9)为前驱体,制备了一种新型多酸盐插层水滑石复合材料(β-SiW9-LDHs)。通过 X线衍射(XRD)、红外光谱(FT-IR)、热重-差热(TG-DTA)、扫描电镜(SEM)和电化学循环伏安法(CV)等手段对目标产物的结构、形貌和性能进行了表征。结果表明,β-SiW9成功插入到 LDH 层间,取代原有硝酸根离子而形成了β-SiW9-LDHs层状复合材料,可望作为酸性、氧化和双功能催化剂。
      Abstract:
      In this paper,we prepared a novel polyoxometalates-intercalated hydrotalcite inorganic com-posite functional material,using Mg-Al Layered Double Hydroxide (LDH)and theβ-Na9HSiW9O34 21H2O (referred to as theβ-SiW9 )as precursors,through the LDH interlamellar anion exchangeability.The struc-ture,morphology and properties of the products were characterized by X-ray diffraction (XRD),infrared spectroscopy(FT-IR),TG-DTA(TG-DTA),scanning electron microscopy(SEM)and electrochemical cyclic voltammetry (CV).The results showed thatβ-SiW9 was successfully inserted into the LDH layers,repla-cing the original nitrate ions,and a new type ofβ-SiW9-LDHs composite was synthetized.
      作者: 杜毛毛 [1] 息春美 [1] 于跃 [2] 温志忱 [2] 张雁锋 [1] 姜春杰 [1]
      作者单位: 辽宁师范大学 化学化工学院,辽宁 大连,116029 中国石油 吉林石化公司合成树脂厂,吉林 吉林,132021
      年,卷(期): 2016, 31(4)
      分类号: O643.36
      在线出版日期: 2017年1月15日
      基金项目: 国家自然科学基金项目